期刊
JOURNAL OF MATERIALS CHEMISTRY A
卷 2, 期 45, 页码 19526-19535出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c4ta03485f
关键词
-
资金
- Australian Research Council [FT100100134]
- Australian Research Council [FT100100134] Funding Source: Australian Research Council
Here we report that the nano La0.6Ca0.4Fe0.8Ni0.2O3-delta (LCFN) decorated Sm0.2Ce0.8O1.9 (SDC) composite oxide, prepared by the solution infiltration method, could function well as a cobalt-free electrode material for symmetrical solid oxide fuel cells (SOFCs). The structure, morphology, thermal expansion, oxygen reduction reaction activity and catalytic activity for methane oxidation of the as-prepared LCFN-infiltrated SDC electrode was investigated systematically. Under a reducing atmosphere, the partial segregation of metallic nickel from the LCFN perovskite lattice was demonstrated by SEM and STEM-EDX, and the XRD results suggested that the perovskite structure of LCFN still survived. Consequently, the good anode performance was expected due to the high catalytic activity of LCFN for methane oxidation and the excellent electrocatalytic activity of nano nickel for the methane reforming and electro-oxidation of hydrogen. In an air atmosphere, an area specific resistance as low as 0.12 Omega cm(2) was achieved at 600 degrees C. The SDC electrolyte supported symmetrical SOFC with the LCFN-infiltrated SDC electrode was then fabricated and tested, which delivered attractive peak power densities of 510 and 350 mW cm(-2) at 800 degrees C, operating on hydrogen and CH4-O-2 fuels, respectively.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据