Significant progress has recently been made in the synthesis of Fe3O4@C nanospheres with uniform, monodisperse and tunable carbon shells. Fe3O4@C nanospheres were obtained by directly carbonizing Fe3O4@polymer which was synthesized by a versatile and economical Stober method with resorcinol and formaldehyde as precursors. The synthesis conditions in the formation of Fe3O4@polymer were systematically investigated. It was found that the yield of the Fe3O4@polymer is highly influenced by the concentration of ammonium hydroxide, and the monodispersity is mainly affected by the concentration of ammonium hydroxide and the citrate group sites outside the surfaces of the Fe3O4 nanospheres. Interestingly, carbonization of Fe3O4@polymer at high temperature makes the grain sizes of Fe3O4 in Fe3O4@C samples larger than those in the Fe3O4 sample, which makes the saturation magnetization value for the Fe3O4@C samples higher than those of common obtained materials. The adsorption performance of Fe3O4@C for anthracene was tested both in water and in cyclohexane solution; it shows fast adsorption rates (about 1 h to reach equilibrium in water and 3 h in cyclohexane solution) and high adsorption capacities (31.5 mg g(-1) in water and 2 mg g(-1) in cyclohexane solution), which are ascribed to its high uniformity and monodispersity. These make Fe3O4@C an ideal adsorption and enrichment material, especially for polycyclic aromatic hydrocarbons in water and in organic solvents.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据