JOURNAL OF MATERIALS CHEMISTRY A
卷 1, 期 19, 页码 6037-6042出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c3ta01638b
关键词
-
资金
- European Commission FP7 project AUTOSUPERCAP
Activated carbon materials are prepared from phenolic resin precursors by physical activation to fabricate electrodes for electric double-layer capacitors (EDLCs). Pore size and surface area of the carbon materials are controlled during the synthesizing process and after the carbonization through activation in a CO2 atmosphere to different levels of burn-off. The resultant carbon materials were evaluated as EDLC electrodes, using electrochemical impedance spectroscopy (EIS) and galvanostatic charge-discharge (GCD) measurements with the organic electrolyte of spiro-(1,1')-bipyrrolidinium tetrafluoroborate in propylene carbonate, SBPBF4/PC. The results of the study showed that the capacitance of carbon materials, as well as energy density of the EDLC cells, increased by increasing the level of burn-off (activation). The 46% activated carbon gave a capacitance of similar to 160 F g(-1) and an energy density of similar to 35 W h kg(-1), at a current density of 1 mA cm(-2). The long term cycling tests showed high cycling stability of these carbon materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据