Reduced graphite oxide-NiFe2O4 (RGO-NiFe2O4) composites were synthesized by adding different amounts of NH3 center dot H2O into a mixed aqueous solution of graphite oxide, Ni(NO3)(2) and Fe(NO3)(3) at room temperature. NH3 center dot H2O was used to adjust the synthesis system's pH value. The morphology and the microstructure of the as-prepared composites were characterized by X-ray diffraction (XRD), Brunauer-Emmett-Teller (BET) and transmission electron microscope (TEM) techniques. The structure characterizations indicate that NiFe2O4 successfully deposited on the surface of the RGO and the morphologies of RGO-NiFe2O4 show a transparent structure with NiFe2O4 homogeneously distributed on the RGO surfaces. Capacitive properties of the synthesized electrodes were studied using cyclic voltammetry and electrochemical impedance spectroscopy in a three-electrode experimental setup using 1 M Na2SO4 aqueous solution as electrolyte. It is found that the pH value plays an important role in controlling the electrochemical properties of these electrodes. Among the synthesized electrodes, RGO-NiFe10 (pH = 10) shows the best capacitive properties because of its suitable particle size and good dispersion property. It could be anticipated that the synthesized electrodes will gain promising applications as novel electrode materials in supercapacitors and other devices by virtue of their outstanding characteristics of controllable capacitance and facile synthesis.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据