期刊
ECS ELECTROCHEMISTRY LETTERS
卷 3, 期 7, 页码 A76-A78出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/2.0081407eel
关键词
-
资金
- EPSRC [EP/I02249X/1, EP/K002252/1]
- EPSRC [EP/I00422X/1] Funding Source: UKRI
- Engineering and Physical Sciences Research Council [EP/K002252/1, EP/I02249X/1, EP/I00422X/1] Funding Source: researchfish
Silicon-Lithium based rechargeable batteries offer high gravimetric capacity. However cycle life and electrode microstructure failure mechanisms remain poorly understood. Here we present an X-ray tomography method to investigate in-operando lithiation induced stress cracking leading to the delamination of a composite Si based electrode. Simultaneous voltage measurements show increased cell resistance correlating with severe delamination and microstructural changes. 3D analysis revealed 44.1% loss of the initial electrode-current collector area after 1 hour of operation at 2.4 mA/cm(2) and a 21.2% increase in new anode surface area. The work represents a new basis for future investigation of Si based anodes. (C) 2014 The Electrochemical Society. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据