期刊
CHEMELECTROCHEM
卷 2, 期 6, 页码 847-851出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/celc.201500021
关键词
carbon supports; fuel cells; nanoparticles; oxygen electroreduction; platinum
资金
- Estonian Target Research Project [IUT20-13]
- Estonian Centre of Excellence in Research Project [3.20101.11-0030]
- Estonian Energy Technology Program project [3.2.0501.10-0015]
- Estonian Materials Technology project [3.2.1101.12-0019]
- Sciex-NMS EFCE project
The electrochemical oxygen reduction reaction (ORR) on bare (100) Pt nanoparticles supported by molybdenum-carbide-derived carbon [(100) Pt-C(Mo2C)] with high specific surface area and controlled microporosity-mesoporosity, pore size distribution, electrical conductivity, and corrosion stability was studied in 0.5m H2SO4 solution by using rotating-disk-electrode and cyclic voltammetry methods. The C(Mo2C) powder was prepared from Mo2C at a fixed chlorination temperature (750 degrees C). Pt nanoparticles were prepared through colloid chemistry and deposited onto/into C(Mo2C) and Vulcan XC72 carbon supports for comparison. The ORR cathodic current densities and half-wave potentials strongly depend on the characteristics of the carbon material used as the support. High values for the ORR current density were calculated for (100) Pt-C(Mo2C) and the half-wave potential is nearly 80 mV more positive compared with that for the (100) Pt-Vulcan XC72 catalyst with a similar catalyst loading.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据