Naturally immiscible PEDOT:PSS and PDMS, which are a typical conducting polymer and an transparent elastomer, respectively, were blended by the support of PDMS-b-PEO. A block copolymer, PDMS-b-PEO, consisting of hydrophobic PDMS backbones and hydrophilic PEO side chains, significantly improved the miscibility of PEDOT: PSS and PDMS. At an optimal PDMS-b-PEO concentration of 30%, a cured PEDOT: PSS: PDMS film was found to be comprised of three-dimensional PDMS networks and a PEDOT: PSS phase filling in between the networks. The optimal blend film exhibited a conductivity comparable to a pure PEDOT: PSS film and a maximum strain to rupture of about 75%. It was also demonstrated that interconnects made of this blend film functioned well irrespective of the substrate and the pattern size, and could reproducibly operate under strains up to 50%. These results indicate that the PEDOT: PSS: PDMS blends could be a practical choice for organic interconnects for future stretchable electronics.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据