Noble metallic foams with low density are desirable in high energy-density physical experiments. In this study, Au foams with ultralow density were successfully synthesized from a template-dealloying approach. Microspherical polystyrene (PS) was employed as the sacrificial template. Au and Ag nanoparticles were sequentially coated onto the PS surface from a three-step deposition process. Cylindrical PS/Au/Ag monoliths were formed by filter-casting of the nanoparticle coated PS suspension. The templates were removed and Au-Ag alloy foams were generated after calcination at 400 degrees C. Self-supported Au foams with bimodal porous structure were produced by dealloying of the less noble Ag component. Au foam with density as low as 0.36 g cm(-3) can be achieved, which demonstrates high surface area of 23.6 m(2) g(-1) and pore volume of 0.15 m(3) g(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据