RSC ADVANCES
卷 4, 期 89, 页码 48632-48638出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c4ra08501a
关键词
-
资金
- National Natural Science Foundation of China [51072013, 51272021, 51142004]
- Natural Science Foundation of Jiangsu Province [BK20131147]
Hydrothermal treatments of electrospun titanium dioxide/carbon nanofibers (TiO2/CNFs) in LiOH solution were performed in a temperature range of 130-190 degrees C, and then followed by a thermal treatment at 600 degrees C in N-2 atmosphere. The changes in morphologies, microstructures and compositions as well as the electrochemical performances with hydrothermal temperatures were investigated for all samples. The morphological and compositional characterizations showed that the surfaces of the CNFs-matrix were covered by numerous nanoparticles with size distributions of 25-100 nm. For the sample hydrothermally treated at 150 degrees C (denoted as LC-150), these nanoparticles (similar to 25 nm) were composed of well-crystalline spinel Li4Ti5O12 and anatase TiO2 with abundant phase interfaces and grain boundaries, which can induce the interfacial pseudocapacitive effect. Therefore, the as-prepared dual-phase structured Li4Ti5O12-TiO2-CNFs sample as a binder-free anode for lithium-ion batteries (LIBs) presented a greatly enhanced reversible capacity (203.8 mA h g(-1) at 100 mA g(-1) after 200 cycles) and a favored rate capability (114.3 mA h g(-1) at 2000 mA g(-1)) compared with the single-phase Li4Ti5O12-CNFs sample.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据