期刊
RSC ADVANCES
卷 2, 期 3, 页码 1174-1180出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c1ra00698c
关键词
-
资金
- AcRF Tier 1 of MOE [RG 31/08]
- Singapore Ministry of Education [MOE2010-T2-1-017]
- A*STAR SERC [1021700144, MPA 23/04.15.03 RDP 009/10/102, MPA 23/04.15.03 RDP 020/10/113]
- [NRF2009EWT-CERP001-026]
Uniform carbon-coated single crystalline vanadium dioxide (VO2(B)@C) nanobelts were successfully prepared by using a facile one-pot hydrothermal approach. Sucrose plays a dual role in this hydrothermal process, namely as a carbon precursor for the carbon shell and, as a reductant to reduce V2O5 to VO2(B). The thickness of the carbon coating layer is tunable from 3.0 to 6.9 nm by changing the ratio of the precursors. Although a high carbon content can improve the electrical conductivity of VO2(B)@C nanobelts, a thick carbon coating layer would block the lithium ion diffusion. The optimal thickness is found to be 4.3 nm (carbon content: 6.6 wt%), where the cathode displays superior performance with highly reversible specific capacities, good cycling stabilities and excellent rate capabilities (e.g. 100 mA h g(-1) at 12.4 C).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据