screen-printed texture-barrier (SPTB); interdigitated back-contact (IBC); photovoltaic silicon solar cells; paste
类别
资金
- National Science Council of the Republic of China [NSC 102-2221-E-150-040, NSC 101-2622-E-150-020-CC3]
Continuous cost reduction of silicon-based solar cells is needed to lower the process time and increase efficiency. To achieve lower costs, screen-printed texture-barrier (SPTB) paste was first developed for single-side texturization (ST) of the interdigitated back-contact (IBC) for silicon-based solar cell applications. The SPTB paste was screen-printed on silicon substrates. The SPTB paste was synthesized from intermixed silicate glass (75 wt %), a resin binder (ethyl cellulose ethoce: 20 wt %), and a dispersing agent (fatty acid: 5 wt %). The silicate glass is a necessity for contact formation during firing. A resin binder and a dispersing agent determine the rheology of the SPTB paste. In this work, by modulating various parameters, including post SPTB firing, alkali texturing, and removal of the SPTB, the ST of IBC silicon solar cells was achieved. Since the advantages of the SPTB paste include low toxicity and prompt formation of the texture-barrier, SPTB is potentially suited for simple fabrication at low-cost for solar cell applications. The cost of the SPTB is around $100/kg which is lower than the SiH4/NH3 gas ambient used in plasma-enhanced chemical vapor deposition (PECVD). Thus, the expensive Si3N4 film deposited by PECVD using SiH4 and NH3 gas ambient for silicon solar cells can be replaced by this SPTB.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据