MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS
卷 195, 期 -, 页码 50-58出版社
ELSEVIER
DOI: 10.1016/j.mseb.2015.02.001
关键词
Magnesium alloy; Processing routes; Hot extrusion; Fine grain strengthening; Corrosion resistance
资金
- National Nature Science Foundation of China [51365029]
- fundamental research funds of Gansu province
- NSF [1006931]
- U.C. Research Laboratories Grant [09-LR-06-118456-MEYM]
It is demonstrated that the mechanical properties and corrosion resistance of Mg-2.5 wt%Zn-1 wt%Ca alloy are enhanced by the microstructural changes imparted by hot extrusion. A processing procedure is developed to form hollow tubes with an outer diameter of similar to 2.0 mm and wall thickness of similar to 0.1 mm, which is well suited for subsequent stent manufacturing. The influence of thermal and mechanical processing on corrosion and plasticity was found to be associated with grain-size reduction and the redistribution of intermetallic particles within the microstructure, providing significant improvement of performance over the cast alloy. Observation of the fracture surfaces reveals a mode transition from brittle (cast) to ductile (processed). Enhanced mechanical properties and decreased resorption rate represent significantly improved performance of this alloy after the novel processing sequence. Based on the improved properties, the produced Mg alloy is more suitable for practical in vivo applications. (c) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据