Hierarchiral NiO flower-like microspheres with tunable porosity were prepared based on a facile solvothermal method. Three kinds of NiO micro-flowers (NiO-A, NiO-B, and NiO-C) with different porosity have been fabricated mainly by tuning the concentration of nickel nitrate. These flower-like microspheres are comprised of densely packed irregular sheets and display a multi-peaks pore distribution in a wide range in both mesoporous and macroporous regions. The BET surface area of NiO-A, NiO-B and NiO-C is 59.9 m(2) g(-1), 50.2 m(2) g(-1) and 15.1 m(2) g(-1), respectively. The pore volume of NiO-A, NiO-B and NiO-C is 0.2214 cm(3) g(-1), 0.0829 cm(3) g(-1) and 0.0549 cm(3) g(-1), respectively. These NiO spheres show a strong morphology dependant nature for CO oxidation catalysis. Compared to the conventional NiO nanoparticles, these flower-like NiO micro-spheres possess a superior catalytic activity for CO oxidation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据