CHEMICAL SCIENCE
卷 9, 期 41, 页码 7968-7980出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c8sc02152j
关键词
-
资金
- EPSRC [EP/L017709, EP/N01572X/1, EP/L000202]
- UCL
- EPSRC [EP/L000202/1] Funding Source: UKRI
Phosphorus doped tin(iv) oxide (P:SnO2) films have been synthesised by an aerosol assisted chemical vapour deposition route. Triethyl phosphate was used as the phosphorus dopant source. The phosphorus concentration in solution was found to be key to electrical properties, with concentrations between 0.25-0.5 mol% phosphorus giving the lowest resistivities of the deposited films. The conductivity of the films synthesised improved on doping SnO2 with phosphorus, with resistivity values of 7.27 x 10(-4) Omega cm and sheet resistance values of 18.2 Omega rectangle (-1) achieved for the most conductive films. Phosphorus doping up to 1.0 mol% was shown to improve visible light transmission of the deposited films. The phosphorus doping also had a significant effect on film morphology, with varying microstructures achieved. The films were characterised by X-ray diffraction, scanning electron microscopy, UV/vis spectroscopy, Hall effect measurements and X-ray photoelectron spectroscopy. The data generated was used to build computational models of phosphorus as a dopant for SnO2, showing that the phosphorus acts as a shallow one-electron n-type donor allowing for good conductivities. Phosphorus does not suffer from self-compensation issues associated with other dopants, such as fluorine.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据