Solid solution is a potential way to optimize thermoelectric performance for its low thermal conductivity compared to those of the constituent compounds because of the phonon scattering from disordered atoms. Tin(II) sulfide (SnS) shows analogous band structure and electrical properties with tin selenide (SnSe), which was the motivation for investigating the thermoelectric performance of SnS and SnS-SnSe solid solution system. SnS compound and SnS1-xSex (0 < x < 1) solid solution were fabricated using the melting method and they exhibited anisotropic thermoelectric performance along the parallel and perpendicular to the pressing directions. For the SnS compound, the maximum zT(parallel to) value is 0.19 at 823 K along the parallel to pressing direction, which is higher than that along the perpendicular to the pressing direction (zT(perpendicular to) = 0.16). The zT values of SnS0.Se-5(0.5) and SnS0.2Se0.8 were higher than those of the SnS compound and a maximum zT value of 0.82 was obtained for SnS0.2Se0.8 at 823 K, which is more than four times higher than that of SnS.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据