JOURNAL OF NATURAL FIBERS
卷 7, 期 2, 页码 100-110出版社
TAYLOR & FRANCIS INC
DOI: 10.1080/15440478.2010.481117
关键词
sisal fibers; coating; strength; DSC; SEM
In this study, the surface of sisal fiber has been modified by coating with different polymers. The influence of surface modification on tensile strength, thermal behavior, storage modulus, and dissipation factors has been determined by using fiber tensile tester, differential scanning calorimetry, and dynamic mechanical analysis. Tensile strengths of uncoated sisal fiber and sisal coated with low-density polyethylene, polystyrene (PS), polyvinyl alcohol, polypropylene, polyester, and araldite epoxy are 593.0, 280, 381, 184.8, 198.3, 273.6, and 104.1 MPa, respectively. In the coated fibers, the maximum tensile strength was found for PS-coated sisal fiber and minimum for epoxy-coated sisal fiber, which is explained based on their fractured microstructures. The storage modulus value of PS-coated sisal fiber determined at 100 degrees C for all frequency was maximum.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据