期刊
WEAR
卷 288, 期 -, 页码 72-77出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.wear.2012.02.009
关键词
Particle shape; Additives; Lubricant; Wear behavior
资金
- National Natural Science Foundation of China [51044011]
La(OH)(3) nanoparticles and serpentine/La(OH)(3) composite particles were synthesized via sol-gel method. The phase compositions, micro-morphology of the synthesized particles were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The tribological properties of different samples were tested and compared by the MM-10W Multi-functional friction abrasion tester and MHK-500 Ring-block wear testing machine. The TEM figure indicates that La(OH)(3) nanoparticles are granular, the average size of the particles is 50 nm. The SEM figure of the composite particles illustrates that La(OH)(3) particles uniformly coat on the surface of serpentine particles. The results of the friction tests indicate that serpentine, La(OH)(3) and serpentine/La(OH)(3) composite particles all exhibit friction-reducing and anti-wear properties compared to the base oil. The oil containing the composite particles have the best friction-reducing, anti-wear and self-repairing properties. The friction coefficients are reduced by 24.63% and the diameters of friction spots are reduced by 41.88% compared to the base oil. The energy spectrum of tribosurface gives evidence of that the contact area of rubbing pair was repaired by composite particles during friction tests. (C) 2012 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据