期刊
WEAR
卷 265, 期 3-4, 页码 461-467出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.wear.2007.11.027
关键词
boundary lubrication; DLC; TOF-SIMS; overbased calcium sulfonate; tribochemistry; runnning-in
The initial stage of boundary film formation from overbased calcium sulfonate at steel-DLC (diamond like carbon) contact was studied. A running-in process was clearly observed by the combination of fresh DLC with fresh steel or fresh DLC with rubbed steel. On the other hand, rubbed DLC does not possess the running-in process. Surface analysis by TOF-SIMS was applied to investigate the formation process and structure of films. It was found that the transfer of iron from the steel ball on to the DLC surface plays a significant role in the formation of boundary film. The depth profile of the film was also obtained by means of an etching technique. The boundary film on steel ball and DLC are mainly composed of iron and calcium oxide. However the depth profiles indicate that distribution of calcium oxide on steel ball is different from that on DLC coated disk. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据