Novel technique for phosphorus recovery from aqueous solutions using amorphous calcium silicate hydrates (A-CSHs)

A novel technique for phosphorus (P) recovery from aqueous solutions was developed using amorphous calcium silicate hydrates (A-CSHs). A-CSHs, which have a high Ca/Si molar ratio of 2.0 or greater, could be synthesized using unlimitedly available, inexpensive materials such as siliceous shale and calcium hydroxide. A-CSHs showed high performance for P recovery from an anaerobic sludge digestion liquor (ASDL) and the synthetic model liquor (s-ASDL) containing 89 mg PO4-P/L. After 20 min mixing, 1.5 g/L A-CSHs could remove approximately 69 and 73% PO4-P from ASDL and s-ASDL, respectively. By contrast, autoclaved lightweight concrete particles, which contained crystalline calcium silicate hydrates as a principal component, removed only 10 and 6% PO4-P, from ASDL and s-ASDL, respectively, under the same experimental conditions. When A-CSHs were washed with deionized water to remove free Ca(OH)(2), P removability was significantly improved (up to 82%) despite the reduction in the amount of Ca2+ released. Unlike in the case of Ca(OH)(2), no significant carbonate inhibition was observed with P removal by A-CSHs. Moreover, P removed by A-CSHs showed better settleability, filterability, and dewaterability than P precipitated with conventional CaCl2 and Ca(OH)(2). The present study demonstrated that A-CSHs have great potential as a novel, beneficial material for P recovery and recycling. (C) 2013 Elsevier Ltd. All rights reserved.