WASTE MANAGEMENT
卷 29, 期 10, 页码 2717-2721出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.wasman.2009.05.015
关键词
-
资金
- Industrial and Research Projects for Undergraduate Students (IRPUS) [1350A05004]
- National Center of Excellence for Petroleum, Petrochemicals and Advanced Materials
- Department of Materials Science and Engineering
- Faculty of Engineering and Industrial Technology, Silpakorn University
- Clean Glass Ltd.
In this Study, wasted glasses from structural glass walls up to 45 wt.% were added into clay mixtures in brick manufacturing process. Physical and mechanical properties of clay bricks were investigated as functions of the wasted glass content and the firing temperature. The results indicated that with proper amount of wasted glasses and firing temperature, clay bricks with suitable physical and mechanical properties could be obtained. The compressive strength as high as 26-41 MPa and water absorption as low as 2-3% were achieved for bricks containing 15-30 wt.% of glass content and fired at 1100 degrees C. When the glass waste content was 45 wt.%, apparent porosity and water absorption was rapidly increased. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据