关键词
Aluminum-doped zinc oxide (AZO) film; Sputtering; Transparent conducting oxide (TCO) film
A hot-cathode plasma sputtering technique was used for fabricating the highly transparent and conducting aluminum-doped zinc oxide (AZO) films on glass substrates from a disk-shaped AZO (Al2O3: 2 wt.%) target. Under particular conditions where the target voltage was V-T = -200 V and the plasma excitation pressure was P-S = 1.5 x 10(-3) Torr, the lowest resistivity of 4.2 x 10(-4) Omega cm was obtained at 400 nm, and this was associated with a carrier density of 8.7 x 10(20) cm(-3) and a Hall mobility of 17 cm(2)/V s. From the annealing experiment of the AZO films in the oxygen and nitrogen gases of the atmospheric pressure it was revealed that both the oxygen vacancies and the grain boundaries in the polycrystalline AZO film played an important role in the electrical properties of the film. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据