ULTRASONICS SONOCHEMISTRY
卷 19, 期 1, 页码 209-215出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.ultsonch.2011.06.004
关键词
Polyol synthesis; Silver nanoparticles; Ultrasonic irradiation; Uniform mixing
资金
- Hoseo University [2010-0115]
A polyol synthesis of silver nanoparticles in the presence of ultrasonic irradiation was compared with other configurations (at ambient temperature, 120 degrees C, and 120 degrees C with injected solutions) in the absence of ultrasonic irradiation in order to obtain systematic results for morphology and size distribution. For applying ultrasonic irradiation, rather fine and uniform spherical silver particles (21 +/- 3.7 nm) were obtained in a simple (at ambient temperature without mechanical stirring) and fast (within 4 min, 3.61 x 10(-3) mol min(-1)) manner than other cases (at ambient temperature (for 8 h, 0.03 x 10(-3) mol min(-1)): 86 +/- 16.8 nm, 120 degrees C (for 12 min, 1.16 x 10(-3) mol min(-1)): 64 +/- 14.9 nm, and 120 degrees C with injected solutions (during 12 min): 35 +/- 6.8 nm; all other cases contained anisotropic shaped particles). Even though the temperature of polyol reaction reached only at 80 degrees C (<120 degrees C) in the presence of ultrasonic irradiation, a uniform mixing (i.e. enhanced collision between silver particle and surrounding components) by ultrasonic irradiation might induce a better formation kinetics and morphological uniformity. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据