Calcium carbonate; Nanoparticles; Lubrication additives; PAO; Tribology
资金
- China National 973 Program [2007CB607606]
- Program of the Light in China's Western Region
- Nature Science Foundation of Gansu [3YS051-A25-003]
This paper reports the tribological behavior of CaCO3 nanoparticles as a green additive in poly-alphaolefin (PAO) base oil under variable applied load, sliding speed, sliding duration, and temperature. The tribological properties and the electrical contact resistance between the tribo-pairs lubricated with PAO alone, and PAO containing CaCO3 nanoparticles, were determined using an Optimol-SRV 4 oscillating friction and wear tester (SRV). The morphology and wear volume of the worn scar were measured simultaneously using a surface profilometer. The results showed that CaCO3 nanciparticles can dramatically improve the load-carrying capacity, as well as the anti-wear and friction-reduction properties of a PAO base oil. In addition, higher applied load, moderate frequency, longer duration time, and lower temperatures are beneficial to the deposition of CaCO3 nanoparticles accumulating on rubbing surfaces. X-ray photoelectron spectroscopy (XPS) reveals a boundary film composed Of CaCO3, CaO, iron oxide, and some organic compounds on the worn surfaces. (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据