ACS SUSTAINABLE CHEMISTRY & ENGINEERING
卷 3, 期 6, 页码 1145-1154出版社
AMER CHEMICAL SOC
DOI: 10.1021/acssuschemeng.5b00073
关键词
Lignin; Polyurethane; Biobased; Coating; Adhesive
资金
- European Commission [FP7-KBBE-2013-7-613802]
New lignin-based thermoset polyurethane (PU) coatings with high lignin content are presented in this work. These materials were obtained by extracting a sol fraction from a raw kraft lignin sample with the bioderived solvent 2-methyltetrahydrofuran (MeTHF), and subsequently directly cross-linking the MeTHF-soluble lignin fraction with a toluene diisocyanate (TDI)-based polyisocyanate at different weight ratios. A thorough characterization of the PU materials highlighted their improved thermal stability, better film forming ability and higher hydrophobic character compared with the un-cross-linked lignin precursor. Additionally, force-distance curve measurements by atomic force microscopy were employed to determine the elastic modulus of the PU materials. Finally, the lignin-based PU materials were found to exhibit high adhesion on different substrates, including glass, wood and metals. The results of this study demonstrate that the direct reaction of chemically unmodified fractionated lignin with polyisocyanates represents an interesting strategy for the development of lignin-based thermoset PU systems that may find application in the field of high-performance biobased coatings and adhesives.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据