ACS SUSTAINABLE CHEMISTRY & ENGINEERING
卷 3, 期 7, 页码 1510-1517出版社
AMER CHEMICAL SOC
DOI: 10.1021/acssuschemeng.5b00219
关键词
Cellulose carbamate; Urea; Conventional heating; Structure; Solubility
资金
- National Natural Science Foundation of China [51273151, 51273067]
- Program for New Century Excellent Talents in University [NCET-11-0415]
- Natural Science Foundation of Hubei Province [2009CDA040]
Cellulose carbamates (CCs) were successfully prepared from cellulose/urea (CU) mixtures based on an easy scale-up method and minimum urea. Urea content and the reaction conditions on the nitrogen content of the reacted CU (RCU) mixtures and CCs were systematically investigated. RCU mixtures and CCs were characterized with elemental analysis, Fourier transform infrared spectroscopy, X-ray diffraction, NMR spectrometry and solubility testing. The result indicated that almost all of urea was involved in the derivatization reaction and cellulose was converted into CC with absence of byproducts. The nitrogen content of CCs increased with an increase of the urea content and the reaction temperature, as well as the reaction time. CCs retained the cellulose I crystalline, and the degree of polymerization hardly changed with the reaction conditions. CCs prepared from CU mixtures with the urea content of 3.4-4.6 wt % displayed good solubility in NaOH/ZnO aqueous solutions. Especially, RCU mixtures without washing could be also well dissolved in NaOH/ZnO solutions and its solubility could reach 97%. This work provided a simple, pollution-free and economic pathway for preparing CCs, which is expected to be useful for the CarbaCell process.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据