TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA
卷 18, 期 2, 页码 378-382出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/S1003-6326(08)60066-7
关键词
silica; aluminum particle; coating; core-shell; oxidation
The silica coated aluminum composite particles were prepared by hydrolysis-condensation polymerization of tetraetbylor-thosilicate(TEOS) on the surface of aluminum particle. The structure, morphology, and properties of the silica coated aluminum were studied. The peaks of Si-O-Si are presented in the Fourier transform infrared (FT-IR) spectrum of the composite particles. The thickness of the silica shell is about 80 nm according to the results of transmission electron microscopy(TEM) and laser particle size analysis, while the mean diameter of the aluminum particle is 7.13 mu m. The mass fraction of silica in the sample was determined by fluorescent X-ray spectrometry(XRF). Result of the thermogravimetric analysis(TGA) indicates that thermal stability of silica coated aluminum particles is better than that of pure aluminum particles at low temperature while more reactive at high temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据