Synthesis and biological characterization of zirconium oxynitride thin film growth by radio-frequency sputtering

Thin films of zirconium oxynitride were grown on common glass, silicon substrates (100) and on stainless steel 316L using the reactive RF magnetron sputtering technique. The films were analyzed through structural, morphological, and biocompatibility studies. The structural analysis was carried out using X-ray diffraction (XRD), and the morphological analysis was carried out using scanning electron microscopy (SEM) and atomic force microscopy (AFM). These studies were done as a function of growth parameters, such as power applied to the target, substrate temperature, and flow ratios. The studies of biocompatibility were carried out on zirconium oxynitride films deposited on stainless steel 316L through proliferation and cellular adhesion. The XRD analysis showed that films deposited at 623 K, with a flow ratio Phi N-2/Phi O-2 of 1.25 and a total deposit time of 30 min grew preferentially oriented along the (111) plane of the zirconium oxynitride monoclinic phase. The SEM analyses showed that the films grew homogeneously, and the AFM studies indicated that the average rugosity of the film was 5.9 nm and the average particle size was 150 nm. Finally, through the analysis of the biocompatibility, we established that the films have a better surface than the substrate (stainless steel 316L) in terms of adhesion and proliferation of bone cells. (C) 2012 Elsevier B.V. All rights reserved.