期刊
THIN SOLID FILMS
卷 520, 期 1, 页码 199-203出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2011.07.021
关键词
Strontium hexaferrite; Sol-gel process; Calcination temperature; Magnetic properties
Strontium hexaferrite SrFe12O19 thin films have been synthesized on the Si (100) substrate using spin coating sol-gel process. The influence of different citric acid to metal ions (CA/MN) molar ratios of 0.5, 1 and 1.5 on the formation of SrFe12O19 was investigated. Fourier transform infrared analysis and theoretical calculations were conducted to determine and help control the concentration of metal citrates in solution precursors. X-ray diffraction, scanning electron microscopy and vibrating sample magnetometer techniques were also applied to evaluate the composition, microstructure, crystallite size and magnetic properties of the SrFe12O19 thin films. The results showed that single phase strontium hexaferrite thin films with optimum physical properties can be obtained from the solution with the CA/MN molar ratio of 1 after calcination at 800 degrees C. The SrFe12O19 thin films synthesized with the CA/MN molar ratio of 1 exhibited crystallite size of 42 nm and isotropically magnetic properties of m(s) =267.5 kA/m (at 795.8 kA/m), M-r= 134 kA/m, and H-c=341.4 kA/m. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据