THIN SOLID FILMS
卷 517, 期 24, 页码 6742-6746出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2009.05.039
关键词
Aluminium; Anodising; Polyaniline; Nanoparticles; Zeta potential; Particle size
类别
资金
- MULTIPROTECT [NMP3-CT-2005-011783]
Coatings, comprising an inner porous anodic alumina film and an outer polyaniline/TiO2 nanoparticle layer, were electrochemically synthesised on an AA2024-T3 aluminium alloy by single-step, anodic polarisation in an oxalic acid-based electrolyte. The morphology and composition of the coatings were examined by TEM, SEM and XPS, with the size and zeta-potential of the TiO2 nanoparticles in the oxalic acid solution also measured. Observation of the growth of the coating during of anodic polarisation revealed that a distinct, two-layered coating is formed from the early stages of polarisation, with the anodic film forming at a constant rate and the outer layer developing at a rate that decreases markedly with times beyond about 30 min. Nanoparticles, agglomerated in the electrolyte, migrate to the anode due to the negative zeta-potential and form the nanoparticle-containing layer at the surface of anodic film. Such particles are not incorporated in the pores due to agglomeration and disordered film porosity at the outer layer of the anodic film. (C) 2009 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据