期刊
THIN SOLID FILMS
卷 516, 期 16, 页码 5590-5596出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2007.07.035
关键词
nickel oxide; reactive sputtering; preferred orientation; electrical properties
Nickel oxide thin films of various preferred orientations were deposited by radio-frequency (RF) magnetron sputtering process in different gas ratios of oxygen atmosphere at RF power 200 W on unheated and heated for (673 K) substrates. The relationships among substrate temperature, preferred orientation and electrical properties of the NiO films were investigated. The resulting films were analyzed by grazing-incidence X-ray diffraction, high-resolution transmission electron microscopy (HR-TEM), and ultrahigh resolution scanning electron microscopy (HR-SEM). The electrical properties were measured using four probe and Hall effects measurements. The results show that films deposited at room temperature with the ratio of oxygen varying from 0 to 100% develop a (111) preferred orientation. At temperature of 673 K, while the (111)-orientated film was obtained under a low ratio of oxygen (< 50% O-2), a (200) preferred orientation was developed under 100% oxygen. The lowest sheet resistance 0.01 M Omega/square, resistivity 0.83 Omega-cm and higher carrier density 7.35 x 10(18) cm(-3) could be obtained on (111) preferred orientation samples prepared on unheated substrates in pure oxygen atmosphere. The relationship between preferred orientation and electrical properties was proposed in this paper. (c) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据