THIN SOLID FILMS
卷 516, 期 15, 页码 4958-4965出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2007.09.047
关键词
III-V compound; BP film; optical properties; PL
We report the physical and electronic properties of BP films of 1: 1, 1: 1.15 and 1.25: 1 stoichiometry prepared by co-evaporating B and P onto glass and Si (100) substrates. Compositional information was obtained from X-ray photoelectron spectroscopy measurements. Optical studies indicated allowed indirect transition at similar to 2.08 eV The room temperature photo luminescence peak at similar to 2.01 eV was due to band gap transitions which shifted to higher energy value when recorded at lower temperature. Fourier transformed infrared (FTIR) spectra were dominated by the characteristic peak of the B-P located at similar to 810 cm(-1) which could be identified as arising due to transverse optical vibration mode (k similar to 0) while the shoulder at similar to 850 cm(-1) may be due to longitudinal optical (k similar to 0) vibration mode. Other characteristic peaks for B-O, P-O and B-H vibration modes were also present in the FTIR spectra. Characteristic Raman peaks for BP located at similar to 415 cm(-1) and 806 cm(-1) were observed in these films. (C) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据