THIN SOLID FILMS
卷 516, 期 7, 页码 1354-1358出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.tsf.2007.03.084
关键词
transparent conducting oxide; thin film; ZnO; AZO; GZO; ITO; stability; moisture-resistant
The stability of nano-thick transparent conducting oxide thin films in a high humidity environment was investigated. The stability of ITO and impurity-doped ZnO thin films prepared with a thickness in the range from approximately 20 to 100 nm on glass substrates at a temperature below 200 degrees C by a pulsed laser deposition was evaluated in air at a relative humidity of 90% and a temperature of 60 degrees C. The resistivity of all Al- and Ga-doped ZnO thin films tested was found to increase markedly with test time, whereas that of ITO remained relatively stable; the stability (resistivity increase) of the doped ZnO thin films was considerably affected by film thickness but was relatively independent of the deposition substrate temperature. In particular, doped ZnO thin films with a thickness below approximately 50 nm were very unstable under the test conditions. The resistivity increase of doped ZnO films is mainly attributed to the grain boundary scattering resulting from the adsorption of oxygen on the grain boundary. (c) 2007 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据