Poly(lactic acid); Reinforcement ligaments; Silica nanoparticles; Montmorillonite; Multi-walled carbon nanotubes; Thermal characterization
Nanocomposites of poly(L-lactic acid) (PLA) with fumed silica nanoparticles (SiO2) montmorillonite (MMT) and oxidized multi-walled carbon nanotubes (o-MWCNTs). containing 2 5 wt% nanoparticles were prepared by solved evaporation method SEM micrographs evidenced fine dispersion of the nanoparticles into PIA matrix This has as result to act as efficient reinforcing agents increasing the storage modulus as was verified from DMA analysis The nanoparticles were found to be effective nucleaging agents in cases of silica nanoparticles and MWCNT On cooling from the melt crystallization was accelerated by the presence of nanoparticles and the effective activation energy calculated using the isoconversional method of Friedmann decreased The nucleation activity was calculated Cold-crystallization was also affected by the presence of nanoparticles However it seems that the phenomenon begins at lower temperatures and this results in formation of imperfect crystalline structure which reduce macromolecular chain mobility of the remaining amorphous polymer finally limiting the ultimate crystallinity (C) 2010 Elsevier B V All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据