关键词
cobalt oxides; thermal analysis; TG-MS
The as-prepared cobalt oxide (assigned as CoOx) was fabricated by precipitation-oxidation from aqueous cobalt nitrate solution using sodium hydroxide and oxidation with hydrogen peroxide. Another series of pure cobalt oxides was refined by the decomposition of CoOx in a nitrogen environment at temperatures of 280, 450 and 950 degrees C (D-280, D-450 and D-950, respectively). Phase transformation, structural properties and red-ox properties were characterized by thermogravimetry-mass spectrometry (TG-MS), X-ray diffraction (XRD), infrared spectroscopy (IR), Raman spectroscopy and temperature-programmed decomposition/reduction (TPD/TPR). Analysis of the thermal behavior on CoOx revealed that a series of pure cobalt oxide with particle sizes of 10-20 nm could be obtained easily. The results demonstrated that the refined samples D-280, D-450 and D-950 were CoO(OH), Co3O4 and CoO, respectively. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据