Tungsten oxide; Microwave irradiation; Poly ethylene glycol; Nanoparticles; L-Dopa; Biosensors
资金
- UGC, Govt. of India
- Department of Science and Technology, Government of India [SR/S5/NM-22/2004]
Nanocrystalline tungsten oxides (WO3-delta) are currently receiving a lot of attention because of their interesting electrical, magnetic, optical and mechanical properties. In this report, we present the synthesis of PEG assisted tungsten oxide (WO3) nanoparticles by simple household microwave irradiation (2.45 GHz) method. The samples were characterized using powder X-ray diffraction (XRD), thermal analysis (TG/DTA), transmission electron microscopy (TEM). UV-visible diffusion reflectance spectroscopy (UV-VIS-DRS), cyclic voltammetry and electrochemical impedance spectroscopy. Powder XRD results revealed that both the samples prepared with and without surfactant crystallize in the orthorhombic structure corresponding to WO3 center dot H2O phase. Subsequent annealing under identical conditions (600 degrees C/air/6h) led to significantly different products i.e. monoclinic W17O47 from surfactant free sample and orthorhombic WO3 from PEG assisted sample. Blue emission was observed through UV-VIS-DRS with blue shift and the band gap energy was estimated as 2.7 and 3.28 eV for PEG assisted as prepared (WO3 center dot H2O) and annealed samples (WO3) respectively. Electrochemical measurements have been performed on all the samples deposited on the surface of glassy carbon (GC) electrode which showed high sensitivity and good selectivity for PEG assisted sample (WO3 center dot H2O) for the direct detection of L-dopa. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据