期刊
SYNTHETIC METALS
卷 176, 期 -, 页码 86-91出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.synthmet.2013.05.033
关键词
PEDOT; Vapor-phase polymerization (VPP); Conductivity; Crystal structure; Grazing angle X-ray diffraction
资金
- National Program on Key Basic Research Project [2010CB934700, 2010CB934502]
- National Natural Science Foundation of China [51003120, 51003119, 11005150, 20973132]
The structure and properties of PEDOT films prepared under different vapor-phase polymerization (VPP) temperatures were characterized by grazing angle X-ray diffraction, Raman spectroscopy, UV/vis absorption, atomic force microscopy, scanning electron microscopy and electrical conductivity measurements. The VPP temperature plays key roles on the polymerization reaction rate and the mobility of the polymer chains as well as the volatilization of the reactant and product, which result in drastically different properties of the VPP PEDOT films. In the range of 33-57 degrees C, the lattice structure and the morphology of the films can be significantly affected by the VPP temperature. The optimum temperature (46 +/- 1 degrees C) resulted in PEDOT film with the highest conductivity on glass substrate (622 S/cm), which is ascribed to highly ordered crystal structure and smooth morphology. After polymerization, the topography, efficiency of current transport and crystal structure of the PEDOT film in response to temperature were in situ monitored by means of conductive AFM and grazing XRD. For PEDOT films with a high level of conjugation, the film conductivity is mainly determined by the crystal structure of the film. The lamella inter-chain stacking order in [1 0 0] direction deeply influences the film conductivity, while the pi-pi stacking order in [0 1 0] direction has no apparent relation with the film conductivity. The film with highly ordered structure in [1 0 0] direction tends to have good film conductivity. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据