期刊
SYNTHETIC METALS
卷 161, 期 5-6, 页码 397-403出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.synthmet.2010.12.017
关键词
Carboxymethylcellulose; Polypyrrole; Conducting films
资金
- French Association Nationale de la Recherche et de la Technologie
The use of carboxymethylcellulose (CMC) in polypyrrole (PPy) synthesis and in the production of PPy freestanding films was investigated. PPy was synthesised by chemical oxidative polymerisation in aqueous solutions using ammonium persulfate CAPS) as oxidant and CMC as conductivity enhancer (CMCd). CMCs with different molar weight, namely 90,000 and 250,000 g/mol, were tested. The influence of polymerisation temperature, time, and CMC concentration, on the conductivity of PPy was evaluated thus showing that higher conductivities were obtained at low temperature, short polymerisation time and in the presence of low molar weight CMC. A long time polymerisation study was carried out at 3 degrees C and 24 degrees C revealing the presence of a double regime polymerisation process, with second regime rates depending on the polymerisation temperature. CMC was also used to improve the limited film forming ability of PPy by dispersing preformed PPy particles in CMC aqueous solutions. When decreasing the weight fraction of film forming CMC, semiconducting, flexible and freestanding films with thickness of 50-100 mu m were obtained and their conductivity increased proportionally to the CMC weight fraction. (C) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据