关键词
IN718; Laser cladding; Coating; Ultrarapid cooling; Microstructure
资金
- National Natural Science Foundation of China [51171116]
IN718 alloy clad coating cooled in liquid nitrogen was fabricated by high power diode laser. The microstructure of the coating was investigated using SEM equipped with energy disperse spectroscopy, and the precipitation phase was analysed using TEM after standard heat treatment. The results showed that the liquid nitrogen provided the clad coating an ultrarapid cooling rate during laser cladding. Laves in the ultrarapid cooled clad coating was refined, and Laves concentration and dendritic space were decreased compared with the air cooled clad coating. The ultrarapid cooling rate reduced the constitutional supercooling and restrained Nb segregation in the Laves during solidification. More Nb was distributed in austenite and precipitated as gamma ''-Ni3Nb during the standard heat treatment to improve the mechanical properties of the clad coating.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据