Nickel; Electrodeposition; EIS; Corrosion
资金
- Board of Research in Nuclear Sciences (BRNS), Mumbai under RTAC [2007/35/13/BRNS/1709]
A comparison was made between the electrochemical corrosion behaviour of electrodeposits prepared from sulphate, sulphamate and Watt's bath on mild steel substrate. Potentiodynamic polarisation tests, electrochemical impedance spectroscopy (EIS), SEM and XRD were the techniques used to characterise the corrosion behaviour. The potentiodynamic studies revealed the current density versus potential for the coated and uncoated substrates and the difference in their corrosion potentials E-corr. In all cases, the E-corr shifted to a more positive potential after the coatings were applied. The EIS measurements as a function of immersion time were carried out in a 3.5% NaCl solution at the E-corr. The corrosion parameters, such as lower corrosion current density I-corr and higher polarisation resistance R-p, were found in coating from sulphamate bath.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据