Nano-MoS2; Composite coating; Electroless plating; Corrosion
资金
- State Laboratory of Solid Lubrication [0401]
- Anhui Provincial Natural Science Foundation [070414152]
Ni-P coatings were co-deposited with MoS2 nanoparticles on medium carbon steel substrate by electroless plating. The effects of incorporation of MoS2 nanoparticles into the Ni-P coating on the morphology of the coating surface and corrosion properties were investigated. X-ray diffraction pattern and X-ray photoelectron spectroscopy spectra showed that the MoS2 nanoparticles were covered in the nickel phosphor matrix. Corrosion tests were conducted in aqueous 10 wt-%HCl, 10 wt-%NaOH and 3.5 wt-% NaCl using a weight loss method, and in aqueous 3.5 wt-% NaCl by electrochemical measurement for bare substrate, Ni-P coating and Ni-P-(nano-MoS2) composite coating, respectively. The experimental results showed that corrosion resistance of the coating containing MoS2 was slightly lower than that of the coating without MoS2. The corrosion rate of Ni-P-(nano-MoS2) composite coating in HCl aqueous solution was found to be increased owing to the corrosion microcells and high porosity and rougher surface. Ni-P-(nano-MoS2) composite coating, however, exhibited significantly enhanced corrosion resistance in both aqueous NaOH and NaCl solutions compared with substrate. The corrosion mechanism of the composite coatings was also discussed.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据