SURFACE & COATINGS TECHNOLOGY
卷 246, 期 -, 页码 34-39出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2014.02.059
关键词
Sol gel; TiO2; Calcination; Wear; CP-Ti
Commercially pure titanium (CP-Ti) is commonly used as an implant material especially for orthopedic and dental treatments in biomedical applications. This material shows insufficient tribological properties. Some surface treatments were applied on surface CP-Ti in order to improve tribological properties of the CP-Ti. Among these techniques, sol-gel coating process was used for this purpose. In this study, CP-Ti was coated by TiO2 film with sal-gel dip coating process. Coated samples were calcined at the various temperatures. The effects of calcination temperature on the wear performance of the coated films were observed. It was observed that the hardness, elastic modulus, surface roughness, friction coefficient and wear resistance values of coated samples were higher than the uncoated CP-Ti values. Also, these properties of coated samples increased with increasing of calcination temperature. The intensity of the rutile-TiO2 phase increased with the calcination temperatures. It was determined that rutile-TiO2 structure showed self-lubrication like behavior. The best tribological properties were obtained from the sample calcinated at 900 degrees C. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据