SURFACE & COATINGS TECHNOLOGY
卷 257, 期 -, 页码 95-101出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2014.01.010
关键词
Hard coatings; TiAlTaN; Arc evaporation; Droplets; Macroparticles; Tribological properties
资金
- Austrian Federal Government
- Styrian Provincial Government
Hard coatings deposited by cathodic arc evaporation are often characterized by droplets, deteriorating their surface roughness and oxidation resistance. Within this work, the response of these droplets to tribological loading and their contribution to the tribological system was investigated. Ball-on-disk tests against Al2O3 counterparts were done on TiAlTaN coated cemented carbide disks at room temperature and 700 degrees C. Surfaces as well as cross-sections through the wear tracks were investigated by scanning and transmission electron microscopy. While droplets were found to contribute to coating degradation by providing nucleation sites for shear cracks and by the release of abrasive fragments into the sliding contact, oxidation at elevated temperature leads to a more efficient embedding into the surrounding coating matrix. This suggests an oxidation induced self-healing process, contributing to the enhanced wear resistance of TiAlN-based hard coatings at elevated temperatures. (C) 2014 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据