期刊
SURFACE & COATINGS TECHNOLOGY
卷 221, 期 -, 页码 111-117出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2013.01.035
关键词
Laser shock processing; Elevated temperature; Residual stress relaxation; Metallographic variation
资金
- National Natural Science Foundation of China [51275556, 51239005]
- Six Major Talent Peak of Jiangsu Province [2012-ZBZZ-025]
The aim of the study was to investigate the influences of laser shock processing (LSP) on residual stress relaxation and metallographic structure evolution of 6061-T651 aluminum alloy at elevated temperature (up to 500 degrees C). Residual stress was determined by XRD with sin(2)psi method, optical microscopy and TEM observations of the grain, and precipitated phase evolutionary process after LSP were carried out. The results showed that the effects of temperature on residual stress relaxation could be described, and the residual stress relaxation was analyzed precisely using the Zener-Wert-Avrami function. The main mechanism of stress relaxation between 200 degrees C to 300 degrees C was the dislocation slip and dislocation climb, and dynamic recovery was the main mechanism during the stress relaxation deformation between 400 degrees C to 500 degrees C. The evolution mechanism of grain and precipitated phase of 6061-T651 aluminum alloy between 25 degrees C and 500 degrees C was proposed. LSP still had a beneficial effect on residual stress at the elevated temperature 300 degrees C. Laser shock processing was the principal element for inducing the metallographic variation (MV) effect of 6061-T651 aluminum alloy at the elevated temperature. (C) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据