SURFACE & COATINGS TECHNOLOGY
卷 226, 期 -, 页码 40-50出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2013.03.034
关键词
TIN and TiCN coatings; Friction; Wear; Tribocorrosion; Artificial seawater
资金
- National Natural Science Foundation of China [51202261]
- Ningbo Municipal Nature Science Foundation [2012A610105]
To improve the tribological performance of sea frictional components, TiN and TiCN coatings, were used for surface protection of the components. The coatings were deposited on stainless steel and WC cemented carbides by arc ion plating. The coating topography was observed using scanning electron microscopy (SEM), and the composition and structure were analyzed by energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). Hardness and adhesion force were tested by nanoindentation and scratch tester, respectively. The friction and wear properties of the TIN and TiCN coatings were investigated by ball-on-disk tribometer in air, distilled water and artificial seawater. The results showed that both the TiCN and TiN coatings had a strong (111) preferred orientation. The friction coefficients of the coatings in distilled water and artificial seawater were lower than those in air. This indicates the influence of aqueous solutions on the friction coefficient due to the lubricative film formed on the coatings. However, the wear loss of the coatings in artificial seawater was larger than those in air and distilled water, this demonstrates a positive synergism between corrosion and wear in artificial seawater. The TiCN coating shows the best wear resistance in the artificial seawater. (c) 2013 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据