SURFACE & COATINGS TECHNOLOGY
卷 206, 期 8-9, 页码 2115-2124出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2011.09.040
关键词
Anodized aluminum; Nanoindentation; Scratch test; Image analysis; Plastic deformation; Elastic behavior
资金
- Spanish Ministry of Education and Science (MEC) [TEC2009-09551]
- CONSOLIDER HOPE [CSD2007-00007]
- AECID [A/024560/09]
- Flemish Science Foundation (FWO)
Mechanical properties like hardness, Young's modulus, and plastic deformation of nanoporous anodized alumina fabricated in the most used acid electrolytes (i.e. sulphuric, oxalic and phosphoric) were extracted from nanoindentation and sliding tests. The dependence of the mechanical properties on the porosity level was analyzed for each type of samples. Nanohardness, Young's modulus and the coefficient of friction were related to the sample type and its porosity. Indents and scratches were inspected by FEG-SEM, which revealed that nanoporous anodized alumina undergo an elastoplastic behavior under the applied loads. The ductility is found to be higher for samples prepared in the phosphoric solution than for the ones obtained from oxalic and sulphuric solutions. This is associated with the high water content, the phosphate anions incorporated into the alumina structure during the anodization process and the aluminum nanopillar structure between those pores with irregular junctions located at the alumina-aluminum interface. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据