SURFACE & COATINGS TECHNOLOGY
卷 205, 期 12, 页码 3651-3657出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2011.01.012
关键词
Nickel; Electrodeposition; Sulfamate bath; Texture; Anisotropy; Back-scattered electron diffraction (EBSD); Indentation
资金
- Swiss Commission for Technology and Innovation [10610.1]
Thick Ni electrodeposits, with thicknesses ranging from 18 to 90 mu m, have been produced from sulfamate baths using very low current densities (1.5-5 mA cm(-2)). Increasing grain sizes, with a corresponding decrease in the hardness values, and more columnar grain morphologies were observed with increasing current densities in the deposits. The anisotropy in the mechanical properties of the deposits were found to correlate strongly with the deposit texture, where the change from a < 101 > dominated orientation at 1.5 mA cm(-2) to a < 001 > orientation at the higher (5 mA cm(-2)) current density led to a corresponding decrease in the indentation modulus values for the respective Ni films. The residual stress values measured in the deposits (75-136 MPa) were found to be comparable to literature values of deposits plated at higher current densities, which rules out any potential advantage from the use of such low current densities for producing lower residual stresses. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据