Electrophoretic deposition; MWCNTs; Nanocomposite coating; Surface charge; Corrosion test
A multi-walled carbon nanotube (MWCNT)/hexamethylene diisocyanate (HDI) composite coating with excellent microstructural homogeneity was produced on copper substrate from aqueous suspensions using electrophoretic deposition (EPD). The concentrations of different additives were optimized to obtain stable suspensions of MWCNT. At the optimum EPD condition, a coating of thickness 170 mu m was obtained at voltage of 30 V and deposition time of 3 min with well dispersed MWCNT in the polymer matrix. The deposit yield increased linearly with deposition time. The adhesive strength of the MWCNT/HDI composite coating was assessed qualitatively by peel test The composite coated specimen showed greater resistance to corrosion in the chloride containing environment with inhibiting efficiency 96.65%. The mechanism for adhered coating is due to better wetting of HDI on copper substrate followed by acid-base reaction between metal hydroxide and polymeric resin. The potential application of the nanocomposite coatings could be protecting copper based metallic structure in marine environment. (C) 2011 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据