SURFACE & COATINGS TECHNOLOGY
卷 205, 期 6, 页码 1789-1792出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2010.05.016
关键词
Magnesium alloy; Microarc oxidation; Lap shear strength; Duty cycle; Porosity
The process of microarc oxidation was studied as a pre treatment for adhesive bonding of magnesium alloys Porous microarc oxidation films on AZ31B magnesium alloy were prepared in a sodium silicate electrolyte by a high frequency bipolar pulsing mode The influences of duty cycle on film porosity and lap-shear strength of the bonding Joints were studied The higher duty cycle increased the film porosity and slightly decreased the thickness of the oxide film The microarc oxidation film consisted mainly of MgO and MgSiO3 The increase of duty cycle resulted in the Increase of MgO in the oxide film As the duty cycle Increased the lap-shear strength increased The highest lap-shear strength 245 MPa was obtained under the duty cycle of 40% The reason was attributed to the larger porosity and enhanced mechanical interlocking effect. (C) 2010 Elsevier B V All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据