期刊
SURFACE & COATINGS TECHNOLOGY
卷 203, 期 9, 页码 1144-1153出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.surfcoat.2008.10.008
关键词
Erosion; Cermets; Thermal spray coating; High temperature deformation; Scanning electron microscopy (SEM)
资金
- Material Performance Technologies (NZ)
- University of Auckland
Cr3C2-NiCr thermal spray coatings are extensively applied to mitigate erosion at temperatures above 450550 degrees C. The aim of this work was to extend the current comparison based knowledge towards a mechanistic interpretation of the high temperature erosion Of Cr3C2 based thermal spray coatings. Coatings that span the range of industrial quality were assessed. They were eroded under high temperature (700 degrees C and 800 degrees C), aggressive (impact velocity 225-235 m/s) conditions designed to simulate the high velocity erodent impacts within a turbine environment. The influence on the erosion response of high temperature induced changes in the coating microstructure and composition with extended in-service exposure was assessed by heat treating selected samples to generate a steady state microstructure prior to testing. In spite of the marked variation in coating microstructure the erosion rates were comparable across the range of coatings tested. The significance of this conclusion is discussed in terms of the erosion mechanism. (C) 2008 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据