Large amounts of slag are generated by the Swedish Steel Industry each year. The Electric Arc Furnace process generates about 200000ton of slag per annum, from which approximately 40% is deposited. An alternative to deposit is to use slag as road construction material. However, leaching of metals from the slag can be a reason to limit slag use in road construction. The aim of this work was to investigate how stable these materials are when aged, in an environment open to seasonable weather conditions, with respect to leaching and mineralogy. Three different EAF-slags from domestic steel plants were used in this study. The materials were characterized after 0, 6, 12, 18, and 24 months to evaluate the ageing process. The analytical techniques that were used to evaluate the effect of ageing are scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and a standard test for leaching. The changes in ageing behavior differ between the three materials. The conductivity and the pH decreases with time for all samples. The leaching of calcium, chromium as well as aluminum decreases with time while the leaching of magnesium increases. CaCO3 was formed on slag surfaces as CaO reacts with moisture and CO2 from the air.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据